ASTM A36 SSAW Dikişsiz Çelik Boru Büyük Çaplı Petrol Çelik Spiral Kaynaklı Boru Boru
  • ASTM A36 SSAW Dikişsiz Çelik Boru Büyük Çaplı Petrol Çelik Spiral Kaynaklı Boru Boru
  • ASTM A36 SSAW Dikişsiz Çelik Boru Büyük Çaplı Petrol Çelik Spiral Kaynaklı Boru Boru
  • ASTM A36 SSAW Dikişsiz Çelik Boru Büyük Çaplı Petrol Çelik Spiral Kaynaklı Boru Boru
  • ASTM A36 SSAW Dikişsiz Çelik Boru Büyük Çaplı Petrol Çelik Spiral Kaynaklı Boru Boru
ASTM A36 SSAW Dikişsiz Çelik Boru Büyük Çaplı Petrol Çelik Spiral Kaynaklı Boru Boru

ASTM A36 SSAW Dikişsiz Çelik Boru Büyük Çaplı Petrol Çelik Spiral Kaynaklı Boru Boru

Menşe yeri Çin
Marka adı TISCO BAOSTEEL
Sertifika SGS BV
Model numarası Karbon Çelik Sac
Ürün Detayları
Adı:
ASTM A36 SSAW dikişsiz çelik boru büyük çaplı yağ çelik spiral kaynaklı boru boru
Uzunluk:
1000-12000mm, Müşterilerin Gereksinimi Olarak
Kalınlığı:
0.5-100mm,6-400mm,1mm-120mm,0.15mm-300mm
Genişliği:
600-2500mm,600mm-1250mm,1.8m,305mm/355mm/455mm/510mm
Yüzey:
Galvanizli Kaplamalı, Siyah Boyalı, PE kaplı, Siyah Boyalı veya Galvanizli, vb.
Malzeme:
a36 A283 A387 1008 4320 SS400 S235jr
Vurgulamak: 

Petrol Çelik Spiral Kaynaklı Boru Boru

,

Büyük Çaplı Dikişsiz Karbon Borular

,

SSAW çelik boru

Ödeme ve Gönderim Koşulları
Min sipariş miktarı
1 Ton
Fiyat
To be negotiated
Ambalaj bilgileri
Kraft kağıt, tahta sandık, müşteri ihtiyaçlarına göre ambalaj
Teslim süresi
Peşin ödemeden 10-15 gün sonra
Ödeme koşulları
L/C, T/T
Yetenek temini
ayda 8000 ton
Ürün Açıklaması

ASTM A36 SSAW dikişsiz çelik boru büyük çaplı yağ çelik spiral kaynaklı boru boru

 

 

ANSI / API 5L, petrol ve doğal gazın nakilinde bir boru hattının kullanımı için dikişsiz ve kaynaklı çelik boruların iki ürün düzeyinin (PSL1 ve PSL2) üretimini belirtir.Ekşi hizmet uygulamasında malzeme kullanımı için, Ek H'ye başvurun; açık deniz hizmetleri için, API 5L 45. baskıdaki Ek J'ye başvurun.

 

Boru üretimi için kullanılan ingotlar, çiçekler, billetler, sarmallar veya plakalar, PSL2 için, bir kabuk rafineri işlemi ile birlikte temel oksijen, elektrikli fırın veya açık şömine ile üretilmelidir.Çelik, ince taneler uygulamasına göre öldürülür ve erdirilir.PSL2 borusu için kullanılan bobin veya plaka herhangi bir onarım kaynakları içermemelidir.

Teslim koşulları

PSL Teslimat Şartları Boru sınıfı
PSL1 Normalleştirilmiş, normalleştirme biçimlendirilmiş A
  Normal olarak yontulmuş, normalleştirme yontulmuş, termomekanik olarak yontulmuş, termomekanik olarak şekillendirilmiş, normalleştirme şekillendirilmiş, normalleştirilmiş, normalleştirilmiş ve ısıtılmış veya sadece anlaşılmış Q&T SMLS B
  Normal olarak yontulmuş, normalleştirilmiş, termomekanik olarak yontulmuş, termomekanik olarak şekillendirilmiş, normalleştirilmiş, normalleştirilmiş ve kalınlaştırılmış X42, X46, X52, X56, X60, X65, X70
PSL 2 Çevirilmiş olarak BR, X42R
  Normalleştirme, normalleştirme şekillendirilmiş, normalleştirilmiş veya normalleştirilmiş ve sertleştirilmiş BN, X42N, X46N, X52N, X56N, X60N
  Saldırılmış ve ısıtılmış BQ, X42Q, X46Q, X56Q, X60Q, X65Q, X70Q, X80Q, X90Q, X100Q
  Termo-mekanik olarak yuvarlanmış veya termo-mekanik olarak şekillendirilmiş BM, X42M, X46M, X56M, X60M, X65M, X70M, X80M
  Termo-mekanik olarak yuvarlanmış X90M, X100M, X120M
  PSL2 sınıfları için yeterli (R, N, Q veya M), çelik sınıfına aittir.  

 

 

PSL 1 borusu için kimyasal bileşim t ≤ 0,984 ′′

 

Çelik sınıfı Sıcaklık ve ürün analizlerine dayanarak % olarak kütle bölümü a,g
C M P S V Nb Ti
en fazla b en fazla b En fazla En fazla En fazla En fazla En fazla
Dikişsiz boru
A 0.22 0.9 0.3 0.3 - Evet. - Evet. - Evet.
B 0.28 1.2 0.3 0.3 c,d c,d d
X42 0.28 1.3 0.3 0.3 d d d
X46 0.28 1.4 0.3 0.3 d d d
X52 0.28 1.4 0.3 0.3 d d d
X56 0.28 1.4 0.3 0.3 d d d
X60 0.28 e 1.40 e 0.3 0.3 f f f
X65 0.28 e 1.40 e 0.3 0.3 f f f
X70 0.28 e 1.40 e 0.3 0.3 f f f
Saldırılmış boru
A 0.22 0.9 0.3 0.3 - Evet. - Evet. - Evet.
B 0.26 1.2 0.3 0.3 c,d c,d d
X42 0.26 1.3 0.3 0.3 d d d
X46 0.26 1.4 0.3 0.3 d d d
X52 0.26 1.4 0.3 0.3 d d d
X56 0.26 1.4 0.3 0.3 d d d
X60 0.26 e 1.40 e 0.3 0.3 f f f
X65 0.26 e 1.45 e 0.3 0.3 f f f
X70 0.26e 1.65 e 0.3 0.3 f f f
a. Cu ≤ = 0,50% Ni; ≤ 0,50%; Cr ≤ 0,50%; ve Mo ≤ 0,15%,
Karbon için belirtilen maksimum konsantrasyonun altında her 0,01% azaltma için, Mn için belirtilen maksimum konsantrasyonun üzerindeki 0,05% artış, en fazla 1'e kadar izin verilir.L245 veya B sınıfları için % 65, ancak ≤ L360 veya X52; > L360 veya X52 sınıfları için en fazla 1,75%, ancak < L485 veya X70; ve L485 veya X70 sınıfları için en fazla 2,00%.
c. Farklı bir anlaşma olmadıkça NB + V ≤ 0,06%
d. Nb + V + TI ≤ 0,15%
e. Aksi bir anlaşma olmadıkça,
Farklı bir anlaşma olmadıkça, NB + V = Ti ≤ 0,15%
B'nin kasıtlı olarak eklenmesine izin verilmez ve geri kalan B ≤ 0,001%

 

 

PSL 2 borusu için kimyasal bileşim t ≤ 0,984 ′′

 

Çelik sınıfı Sıcaklık ve ürün analizlerine dayanarak % olarak kütle bölümü Karbon Eşitliği a
C Evet. M P S V Nb Ti Diğerleri CE IIW CE Pcm
en fazla b En fazla en fazla b En fazla En fazla En fazla En fazla En fazla En fazla En fazla
Dikişsiz ve kaynaklı boru
BR 0.24 0.4 1.2 0.025 0.015 c c 0.04 E,l 0.43 0.25
X42R 0.24 0.4 1.2 0.025 0.015 0.06 0.05 0.04 E,l 0.43 0.25
BN 0.24 0.4 1.2 0.025 0.015 c c 0.04 E,l 0.43 0.25
X42N 0.24 0.4 1.2 0.025 0.015 0.06 0.05 0.04 E,l 0.43 0.25
X46N 0.24 0.4 1.4 0.025 0.015 0.07 0.05 0.04 D,e,l 0.43 0.25
X52N 0.24 0.45 1.4 0.025 0.015 0.1 0.05 0.04 D,e,l 0.43 0.25
X56N 0.24 0.45 1.4 0.025 0.015 0.10f 0.05 0.04 D,e,l 0.43 0.25
X60N 0.24f 0.45f 1.40f 0.025 0.015 0.10f 0.05f 0.04f G,h,l Anlaştığımız gibi
BQ 0.18 0.45 1.4 0.025 0.015 0.05 0.05 0.04 E,l 0.43 0.25
X42Q 0.18 0.45 1.4 0.025 0.015 0.05 0.05 0.04 E,l 0.43 0.25
X46Q 0.18 0.45 1.4 0.025 0.015 0.05 0.05 0.04 E,l 0.43 0.25
X52Q 0.18 0.45 1.5 0.025 0.015 0.05 0.05 0.04 E,l 0.43 0.25
X56Q 0.18 0.45f 1.5 0.025 0.015 0.07 0.05 0.04 E,l 0.43 0.25
X60Q 0.18f 0.45f 1.70f 0.025 0.015 g g g H,l 0.43 0.25
X65Q 0.18f 0.45f 1.70f 0.025 0.015 g g g H,l 0.43 0.25
X70Q 0.18f 0.45f 1.80f 0.025 0.015 g g g H,l 0.43 0.25
X80Q 0.18f 0.45f 1.90f 0.025 0.015 g g g i,j Anlaştığımız gibi
X90Q 0.16f 0.45f 1.9 0.02 0.01 g g g J,k Anlaştığımız gibi
X100Q 0.16f 0.45f 1.9 0.02 0.01 g g g J,k Anlaştığımız gibi
Saldırılmış boru
BM 0.22 0.45 1.2 0.025 0.015 0.05 0.05 0.04 E,l 0.43 0.25
X42M 0.22 0.45 1.3 0.025 0.015 0.05 0.05 0.04 E,l 0.43 0.25
X46M 0.22 0.45 1.3 0.025 0.015 0.05 0.05 0.04 E,l 0.43 0.25
X52M 0.22 0.45 1.4 0.025 0.015 d d d E,l 0.43 0.25
X56M 0.22 0.45f 1.4 0.025 0.015 d d d E,l 0.43 0.25
X60M 0.12f 0.45f 1.60f 0.025 0.015 g g g H,l 0.43 0.25
X65M 0.12f 0.45f 1.60f 0.025 0.015 g g g H,l 0.43 0.25
X70M 0.12f 0.45f 1.70f 0.025 0.015 g g g H,l 0.43 0.25
X80M 0.12f 0.45f 1.85f 0.025 0.015 g g g i,j .043f 0.25
X90M 0.1 0.55f 2.10f 0.02 0.01 g g g i,j - Evet. 0.25
X100M 0.1 0.55f 2.10f 0.02 0.01 g g g i,j - Evet. 0.25
a. SMLS t> 0,787, CE sınırları sözleşildiği gibi olacaktır. C > 0,12% için uygulanan CEIIW sınırları ve C ≤ 0,12% için CEPcm sınırları uygulanır.
b. C için belirtilen maksimumdan %0,01 daha düşük her bir azaltma için, Mn için belirtilen maksimumdan %0,05 daha fazla bir artış, L245 veya B sınıfları için en fazla %1,65'e kadar izin verilir.ama ≤ L360 veya X52L360 veya X52'den büyük, ancak L485 veya X70'den küçük sınıflar için en fazla 1,75%'e kadar; L485 veya X70'den büyük, ancak L555 veya X80'den küçük sınıflar için en fazla 2,00%'e kadar; ve L555 veya X80'den büyük sınıflar için en fazla 2,20%'e kadar,
c. Farklı bir anlaşma olmadıkça Nb = V ≤ 0,06%
d. Nb = V = Ti ≤ 0,15%,
e. Aksi anlaşılmadığı sürece, Cu ≤ 0,50%; Ni ≤ 0,30% Cr ≤ 0,30% ve Mo ≤ 0,15%,
f. Aksi bir anlaşma olmadıkça,
Farklı bir anlaşma olmadıkça, Nb + V + Ti ≤ 0,15%
Aksi anlaşılmadığı sürece, Cu ≤ 0,50% Ni ≤ 0,50% Cr ≤ 0,50% ve MO ≤ 0,50%,
i. Aksi bir anlaşma olmadıkça, Cu ≤ 0,50% Ni ≤ 1,00% Cr ≤ 0,50% ve MO ≤ 0,50%,
j. B ≤ 0,004%,
Aksi bir anlaşma olmadıkça, Cu ≤ 0,50% Ni ≤ 1,00% Cr ≤ 0,55% ve MO ≤ 0,80%,
l. Not j ile belirtilen sınıflar hariç tüm PSL 2 boru sınıfları için aşağıdakiler geçerlidir. Aksi bir anlaşma olmadıkça, kasıtlı olarak B eklenmesine izin verilmez ve geri kalan B ≤ 0,001%.

 

Mekanik özellikler

 

Boru sınıfı Çekim özellikleri SMLS ve kaynaklı boruların boru gövdesi PSL 1 Dikişli boru dikişleri
Üretim Gücü Çekim Gücü a Uzunluk Çekim Gücü b
Rt0,5 PSI Min Rm PSI Min (A % min içinde) Rm PSI Min
A 30,500 48,600 c 48,600
B 35,500 60,200 c 60,200
X42 42,100 60,200 c 60,200
X46 46,400 63,100 c 63,100
X52 52,200 66,700 c 66,700
X56 56,600 71,100 c 71,100
X60 60,200 75,400 c 75,400
X65 65,300 77,500 c 77,500
X70 70,300 82,700 c 82,700

 

 

Hidrostatik test

 

Boru, kaynak dikişinden veya boru gövdesinden sızmadan hidrostatik bir teste dayanır.

Eğiliş testi

 

Test parçasının herhangi bir bölümünde çatlak oluşmamalı ve kaynak açılmamalıdır.

Düzleştirme testi

 

Düzleştirme testi için kabul kriterleri şunlardır:

  • EW boruları D<12.750 in:
  • X60 ile T 500in. Plaklar arasındaki mesafe orijinal dış çapın% 66'sından daha az olmadan önce kaynak açılmamalıdır. Tüm sınıflar ve duvarlar için% 50.
  • D/t > 10 olan borularda, levhalar arasındaki mesafe orijinal dış çapın %30'undan daha küçük olmadan kaynak açılmamalıdır.
  • Diğer boyutlar için tam API 5L spesifikasyonuna bakın.

 

 

ASTM A36 SSAW Dikişsiz Çelik Boru Büyük Çaplı Petrol Çelik Spiral Kaynaklı Boru Boru 0

 

ASTM A36 SSAW Dikişsiz Çelik Boru Büyük Çaplı Petrol Çelik Spiral Kaynaklı Boru Boru 1 

Ödeme Şartları

1Ödeme: T/T, L/C, Western Union, MoneyGram, PayPal; %30 depozit; teslimattan önce %70 bakiye.

2. MOQ: 1pcs

3Garanti: 3 yıl

4Paket Bilgileri: 1) İHA, 20 feet (GW 25 ton) veya 40 feet konteyner (GW 25 ton)

2) Müşterinin gereksinimine göre

 

Neden bizi seçtin?

(1) Çin özel çelik endüstrisinde önde gelen ihracatçı.

(2) Çeşitli boyutlar için büyük stoklar, hızlı teslimat tarihi.

(3) Çin'in ünlü fabrikalarıyla iyi iş ilişkileri.

(4) 7 yıldan fazla çelik ihracat deneyimi.

(5) Satış sonrası iyi hizmet garantisi.

Etiketler:

siyah çelik dikişsiz boru astm a106,

0.8mm siyah çelik dikişsiz boru,

8 inç astm a106 dikişsiz boru

Önerilen Ürünler

İstediğiniz Zaman Bize Ulaşın

+86 18762819931
G16, 66 Chunhui Middle Road, Xishan Ekonomik Kalkınma Bölgesi, Wuxi şehri, Çin
8618762819931
sales03@laiyuan-steels.com
Sorgunuzu doğrudan bize gönderin